Rich Royal
Definition
High stability and super quality inks for high speed machines for commercial printing and packaging.
RICH ROYAL is the fast setting and quick drying sheetfed process series, which is suitable for wide range of absorbent substrates, due to its high resistance to mechanical stress. The strong, pure hues, in combination with ideal trapping characteristics ensure a captivating contrast of the printed image.
Physical parameter:
| Rich Royal | Tack Value | Drying time | Setting time | Rub resistance | Gloss @60 | |
|---|---|---|---|---|---|---|
| Unit GM | Art paper | Glass plate | R.I. Tester | Low+++++high | Low+++++high | |
| Yellow | 8-9 | 3-4 min | 5 hrs. | 5-6 min | ++++ | ++++ |
| Magenta | 9-10 | 3-4 min | 5 hrs. | 4-5 min | +++ | ++++ |
| Cyan | 9-10 | 3-4 min | 4 hrs. | 4-5 min | ++++ | ++++ |
| Black | 9-10 | 3-4 min | 5-6 hrs. | 4-5 min | +++ | ++++ |
Tack values @30C on Thwing- Albert ink-o-meter at 800rpm
Drying on glass plate- cube applicator(38µm) Oven-70⁰C
| Rich Royal | Product Code | Light (BWS)1----------8 scale | Alcohol ISO 2836 | Solvent mixture ISO 2836 | Alkali ISO 2836 |
|---|---|---|---|---|---|
| Yellow | AP6291 | 4 | + | + | + |
| Magenta | AP6292 | 4 | + | + | - |
| Cyan | AP6293 | 8 | + | + | + |
| Black | AP6294 | 8 | + | + | + |
Above lightfastness values refer to solid printing. Lightfastness decreases at low ink density or halftone printing. Intermixed colours will give low lightfast values.
Press Performance:
- Good rheological behavior
- Easy to use-quick and stable ink-water balance
- Suitable for all dampening systems
- Duct-fresh
Print Performance:
- Optimum gloss
- Optimum setting speed
- Colour shade according to DIN ISO 2846-1 and ISO 12647-2
- Minimal dot gain and very good colour reproduction
- Moderate rub resistance
Varnishability:
Printed sheets with Rich Royal can be overprinted either with an oil based overprint varnish or a water based overprint varnish.
Available packing:
2kg conical metal tins(8x2kg carton)
Storage:
Advisable to use in one year after manufacturing as being stored and transported at ambient temperature and humidity.